Chunk of wood ID

[Dave Shepard]

I've been chiselling away at a timber off and on for the last week. Section is about 6"x7" Trying to figure out what it is. It's dense, hard, mean, probably slow growing, has a really severe case of interlocking grain, it's DanG hard, laughs at edge tools, looks a lot like black locust, although without the yellow tint, and in general completely lacks any outwards signs of cooperation. Here are a couple of bad photos. Good luck. :D

[pigman]

 I am not good at IDing wood, but I happened to be on at the right time so I get to have the first guess. I guess notsweetgum. ;D

[Dave Shepard]

This chunk of wood most likely started growing in Fulton County, New York, probably in the late 1600's. It's present excellent condition leads me to believe that this species of wood must possess a resistance, if not total immunity, to any saprophyte living then or now in it's original habitat. Whatever it's green working properties are, they are a mystery long hidden by nearly a quarter of a millennium of brooding meanness and obstinacy.

[blaze83]

my vote is for Red elm,   just because it fits the above description 8)

[Dana]

American Chestnut? Looks like it's a reclaimed beam or railroad tie with creosote treatment.

[Dave Shepard]

Elm is not a bad guess, we are leaning in that direction as well. Definitely not a railroad tie, this timber is from a barn built in 1801, and it is recycled from a hay barrack that could be much earlier. To heavy and mean natured for chestnut.

[SwampDonkey]

My guess is ship mast quality black locust, which is darker heart. Also has some banding of late wood pores similar to pattern in elms, but not as densely spaced. Baring that, Osage if you can get the extractives to leach out of shavings in hot water.  ;D

[rambo]

I have not a clue. But I think it is cool that we are so awe struck by that piece. thanks for sharing.

[WDH]

I am with Dana on the chestnut.

[SwampDonkey]

Chestnut would be my second guess, but doesn't sound like it so much with all the grief tooling it. Chestnut is not very hard and heavy either, but rot resistance is pretty good. The wood does look oak-like on that side shot. I'm still leaning hard on locust though. ;D

[Dana]

Dave if it came out of a barn, it's possible manure stained the wood a deep walnut color. I would be surprised if it would go that deep into a timber. But, you never know. This is a photo of what I was told is old growth chestnut. My Uncle made a bench out of it the black staining from nails in the wood. The lumber was reclaimed from a barn. No manure though.

NOTE:  This is not Chestnut. It has been identified as an oak (for those of you who don't read all of the thread)

[SwampDonkey]

Looks like red oak Dana, because those wood rays on the end would be almost impossible to see with a hand lens if it were American chestnut.

[woodtroll]

Looks like old osage to me.

[WDH]

Dana,

What you have is definitely positively not chestnut because of the wide rays like SD points out.  It is an oak.

[Dana]

We darn it, you guys have sure spoiled my heirloom and the story that went with it. :-\ On the plus side, at least now I know for sure what it is.

[Tom]

Dave Shepard's first post.

When I opened this thread a little while ago, and saw that picture in post #1, I said to myself,  "Dang!, that's pine!".   It sure looks like a piece of resin impregnated SYP (fat lighter) to me.   That stuff is harder'n Chinese arithmetic.

[SwampDonkey]

The grain isn't pine though Tom, if you look at the second picture. It's ring porous.

[LeeB]

Ash maybe?

[Ron Wenrich]

The grain isn't pine though Tom, if you look at the second picture. It's ring porous.

The end cut doesn't look to be very ring porous.  I'm assuming that the side cut is a very old and not a freshly cut piece.  How much of the old wood would slough off over the years and give the appearance of ring porous?  Just a thought.

My first impression of the side cut is chestnut.  But, the end cut doesn't look quite right.  I like Tom's direction with SYP, but point more to NYP.  Pitch pine could fit that bill, as it would be in the range of NY.  Some of that stuff was pretty heavy, and it didn't rot much.  Add the slow growth factor in there and you get some pretty dense stuff.

[SwampDonkey]

The end cut is hard to tell for truths sake because it's too grainy to see detail. But the side shot is very porous in texture. I still don't think it's chestnut either, I will still say mast grade locust just to be different. ;)  :D

I guess as far as knowing how wood would behave after 150 years in a barn you'd have to have some experience dealing with it. Of course this assumes you know what your dealing with in the first place. ;) But, I have my doubts pine would have a porous texture over time without disintegrating. Something would have to break down. ;)

Chestnut I believe has really large early wood pores and invisible rays.

[Dave Shepard]

The architect I'm working with is a good wood ID guy. He uses Hoadley's books as well as his own experience. The side shot is from a block that I split some off of. It is very locust like. There is some bark on one piece, and it looks a lot like elm. Wouldn't pitch pine smell like turpentine? This doesn't have any pine smell. It does have a smell, I can't place it. Pitch pine (pinus rigida) was used in New World Dutch Barns, in fact we drove through a stand of it last week on the Thruway on the way out to look at another Dutch barn. This barn was also mostly white pine, but had some oak and the long purlin braces were of the same wood that we are discussing here. I took some shots of the barn when they unloaded it on Wednesday. Here is a shot of one of those long braces. I'll be at work tomorrow, so I'll try to get some better bark shots.

[Chuck White]

I would say that the wood is HEMLOCK.

Especially going by the first photo.

[Dave Shepard]

I was able to get a fair close-up of the wood in question. First is the uncropped photo. The piece is 1/2" thick and has 8 rings. That is the largest spacing on rings I could find. There are some bands in the wood that are just the holes, with no apparent individual rings. I'm guessing there was a pattern of suppression and release over the course of the trees life. Second shot is a crop of the first. I hope the image quality holds up. Hopefully this well shed some light on the situation.

[SwampDonkey]

Looks ash-like, fine rays and solitary late wood pores, tyloses in early wood pores. Kind of dark though, should be more grayish brown for white ash. Not very rot resistant. Was thinking sassafras, but the pore pattern is not right in the latewood. Ash is quite tough stuff in my experience.

[SwampDonkey]

Slow growing white ash.

[SwampDonkey]

Closeup view. ;D

[Dave Shepard]

I think you may have it SD. I compared my photo to the Hoadley photos for white and black ash. Looks like white to me. Early on I had compared the tangential section to white ash, but wasn't sure. Now, I am more confident. I tried to look at a piece of white ash here, but couldn't see it as well as the photo. I may try to get another photo of some known white ash at work where I have my "laboratory" equipment, i.e. a sharp chisel and a tripod for my camera. :D

[LeeB]

Ash maybe?

Somebody already mentioned ash.  :

[SwampDonkey]

Leeb, I'll give ya credit.  ;D But, the comparison photos help. ;)

[SwampDonkey]

Dave, those rays are hard to see without a little moisture and a hand lens.

[LeeB]

Leeb, I'll give ya credit.  ;D But, the comparison photos help. ;)

That they do, I based my guess on the original photo though. It looks like red oak but it ain't, so to me that leaves poor man's oak, Ash.

[SwampDonkey]

Was that a wild ash guess or a serious one? ;) :D

[LeeB]

I wouldn't call it wild, I did put a little thought into it and put forward what I thought was a good posibilty, but it weren't any where near serious.

[SwampDonkey]

Well you did good, how ever you approached it.  ;)

[SwampDonkey]

I don't know if you can see the luster on the strips in the bed of the sled, but it shines pretty good after planing.

[Ironwood]

Those tyloses are curious. Ash? I dunno.

Ironwood

[WDH]

I am with Lee on the ash.  The color says chestnut, but the density and pore pattern says ash.  In ash, there are usually parenchyma cells that circle the latewood pores, and I think that I see that in the close up photo.

[Tom]

that's a cool looking sled.  We don't use them around here, so I'm no judge as to whether it is built well or not, but It sure is pretty.  It looks like it would work too.  Do you wax the runners?  Do you paint the rest?

Is that one like the dogs pull?  What kind of load will it carry?  What would be the dollar value of one, if it were store-bought?

[Dave Shepard]

WDH, is this any better? I should have soaked the sample before I sliced the end, I think it would have cut better.

[LeeB]

I can't help it, I'm a redneck at heart. I wat to know if you can pull the sled with a four wheeler?  ;D

[LeeB]

I wonder if the beam where soaked with some kind of oil such as coal oil or deisel that turned it so dark? After this many years surely the voc's would be long since evaporated and not leave a scent as a clue.

[Dave Shepard]

I would be surprised if they were Lee. We have two Dutch barns from two different counties in New York state, and they both have this wood in them. The black ash photo in Hoadley's book is darker than the white ash photo. I'm getting another lens for the camera I think this week. It may allow me to get close enough to see those parenchyma.

[LeeB]

I don't really know much about ash as I have never been around any. I'm just throwing out guesses and trying to get answers to better educate myself.

[SwampDonkey]

It's ash alright, nothing else fits. But, black ash is light like American elm when dry. White ash is heavy and hard and lustrous, black is dull when worked, no luster. There are parenchyma joining some pores in the white ash and they don't usually do that in black. If you look close to my picture, some looked linked in a chain of pores in the late wood by the parenchyma. Dave's are more solitary, so I would say he has black ash there along with the brown heartwood. White ash would have light yellow streaks in the heartwood, not as dark as black ash.

[SwampDonkey]

that's a cool looking sled.  We don't use them around here, so I'm no judge as to whether it is built well or not, but It sure is pretty.  It looks like it would work too.  Do you wax the runners?  Do you paint the rest?

Is that one like the dogs pull?  What kind of load will it carry?  What would be the dollar value of one, if it were store-bought?

Tom your a champion. :D

Building an Arctic Slow Sled for some winter fun.  ;D  It's not a dogsled, but dogs could well haul it as a team. You'll have to submerge yourself in the thread to answer some of your other questions. ;)

[Tom]

I'm already up to my blub...blub....blub.......           :D

[Dave Shepard]

It's black ash. Confirmed by R. Bruce Hoadley.

[SwampDonkey]

Also, note that hardwood rays are made entirely of parenchyma cells except an aggregate ray (combination of closely spaced rays, fibers and vessels).